DeWAL D/W 213
聚四氟乙烯
DeWAL Industries
產(chǎn)品說明
D/W 213 is a film skived from virgin PTFE, that has been etched on one side with Sodium Naphthalene (D/W212) after which a primer has been applied to enhance bonding to elastomers and pressure sensitive adhesives. This surface treatment allows the PTFE which normally exhibits very poor adhesion to be bonded to other materials. The primer may be specified by the end user or may be recommended by DeWAL for specific applications.
The primary applications for sodium etched PTFE involve bonding to elastomers to produce laminated diaphragms, as well as the applicaton of pressure sensitive adhesives in the production of PTFE pressure sensitive tapes.
總體
材料狀態(tài) • 已商用：當(dāng)前有效
供貨地區(qū) • 北美洲 • 歐洲
性能特點(diǎn) • 良好粘結(jié)性
用途 • 薄膜 • 隔膜
• 帶子 • 粘合劑
外觀 • 白色 • 紅色
• 黑色 • 自然色
形式 • 薄膜
物理性能 額定值單位制
Thickness 50.8 到 1020nm
薄膜 額定值單位制 測試方法
抗張強(qiáng)度 - MD (屈服) 27.6MPa ASTM D882
伸長率 - MD (斷裂) 300% ASTM D882
熱性能 額定值單位制
最高連續(xù)使用溫度 260°C
補(bǔ)充信息 額定值單位制
Core ID 7.62cm
Maximum Roll OD 356mm
Width 305 到 965mm
備注
1 一般屬性：這些不能被視為規(guī)格。