DeWAL D/W 502
聚四氟乙烯
DeWAL Industries
產(chǎn)品說明
D/W 502 is a skived, tensilized PTFE (Polytetrafluoroethylene) film held to close tolerance on width and thickness. D/W 502 conforms to Mil-P-22241B. The tensilizing process yields a film with greatly enhanced tensile and dielectric strength.
D/W 502 finds use in electrical applications where high temperature service rating and superior electrical properties are desired. Examples of electrical applications include capacitor films, harnesses for electrical wiring in automotive and aerospace applications, spacers for transformers and other electrical insulation applications where high dielectric strength and high temperature resistance are requisite.
總體
材料狀態(tài) • 已商用：當(dāng)前有效
供貨地區(qū) • 北美洲 • 歐洲
性能特點(diǎn) • 高拉伸強(qiáng)度 • 良好的電氣性能 • 耐熱性，高
用途 • 電氣/電子應(yīng)用領(lǐng)域 • 航空航天應(yīng)用
• 電器導(dǎo)線絕緣材料 • 汽車領(lǐng)域的應(yīng)用：
形式 • 薄膜
物理性能 額定值單位制
Thickness 50.8 到 127nm
薄膜 額定值單位制 測(cè)試方法
抗張強(qiáng)度 - MD (屈服) 124MPa ASTM D882
伸長(zhǎng)率 - MD (斷裂) 100% ASTM D882
熱性能 額定值單位制
最高連續(xù)使用溫度 260°C
電氣性能 額定值單位制 測(cè)試方法
介電強(qiáng)度 160kV/mm ASTM D149
補(bǔ)充信息 額定值單位制
Core ID 7.62cm
Maximum Roll OD 356mm
Width 6.35 到 508mm
備注
1 一般屬性：這些不能被視為規(guī)格。