NEOFLON™ AC-5820
全氟烷氧基
DAIKIN AMERICA, INC.
產(chǎn)品說(shuō)明
NEOFLON Coating Powder is a high performance material made from fluoropolymer resin.
Two kinds of NEOFLON Coating Powders, NEOFLON FEP, and PFA Coating Powder, are available.
NEOFLON FEP Coating Powder is a fine powder made of tetrafluoroethylene and hexafluoropropylene copolymer and NEOFLON PFA Coating Powder is a fine powder made of tetrafluoroethylene and perfluoroalkylvinylether copolymer.
NEOFLON FEP and PFA Coating Powder are low in melt viscosity and excellent in melt fluidity which can give a coating free of pinholes. NEOFLON FEP and PFA are ideal for use as corrosion resistant linings because of their excellent thermal and chemical resistance properties.
總體
材料狀態(tài) • 已商用：當(dāng)前有效
供貨地區(qū) • 北美洲
• Good Corrosion Resistance • 高 ESCR（抗應(yīng)力裂紋） • 良好的流動(dòng)性
性能特點(diǎn) • High Purity • 抗燃 • 耐化學(xué)性良好
• 低粘度 • 良好的電氣性能 • 耐氣候影響性能良好
用途 • 襯里 • 涂敷應(yīng)用
外觀 • 白色
形式 • 粉狀
加工方法 • 滾塑成型 • 涂層
物理性能 額定值單位制 測(cè)試方法
比重 2.12 到 2.17g/cm³ ASTM D792
表觀密度 0.75 到 1.05g/cm³ JIS K6891
熔流率 (372°C/5.0 kg) 5.0 到 7.0g/10 min ASTM D3307
顆粒大小 2 150 到 250µm
機(jī)械性能 額定值單位制 測(cè)試方法
抗張強(qiáng)度 19.6 到 31.4MPa JIS K6888
伸長(zhǎng)率 (斷裂) 250 到 350% JIS K6888
摩擦系數(shù) (與自身 - 靜態(tài)) 0.050 到 0.080 Internal Method
抗泰伯磨耗 (CS-17 轉(zhuǎn)輪) 5.00 到 15.0mg
硬度 額定值單位制 測(cè)試方法
硬度計(jì)硬度 (邵氏 D) 60 ASTM D2240
熱性能 額定值單位制 測(cè)試方法
熔融溫度 303 到 313°C ASTM D3307
補(bǔ)充信息 額定值單位制
Adhesion Strength - Peel Test 3 4.0 到 6.0kN/m
Contact Angle 4
Hexadecane 65.0°
Water 102 到 106°
備注
1 一般屬性：這些不能被視為規(guī)格。
2 Laser Diffraction
3 1) steel substrate are roughened with 80 ~ 120 mesh sand 2) applied two coat primer EK-1083G,EK-1883GB
3) applied NEOFLON Coating Powder into 500 µm thickness.
4 Goniometer
|