Tefzel 750
乙烯四氟乙烯共聚物
DuPont Fluoropolymers
產品說明
DuPont™ Tefzel ® fluoropolymer resins offer mechanical strength and toughness along with resistance to heat and chemicals. In addition, they provide easy processing, high specific dielectric strength, and a low coefficient of friction. For these reasons, Tefzel ® resins are widely used to make compact wire and cable constructions that provide long, reliable service in demanding environments.
Tefzel ® 750 retains the traditional characteristics of Tefzel ® resins while providing some new property advantages, including increased flexibility and improved retention of properties after aging at elevated temperatures, higher limiting oxygen index, and long-term service life at higher temperatures than other Tefzel ® resins.
Underwriters Laboratories, Inc. (UL) has rated wire insulated with Tefzel ® 750 (10 mil for 600V, 6 mil for 300V) for service in appliances at a maximum continuous operating temperature of 200°C (392°F). This rating was determined under the guidelines of UL Subject 758 for appliance wiring material. Upper service temperatures for other applications should be determined under the guidelines for those applications. Temperature ratings may not be the same as the rating for appliance wire because the test procedures are different.
總體
材料狀態 • 已商用：當前有效
供貨地區 • 北美洲 • 歐洲
• 南美洲 • 亞太地區
性能特點 • 低摩擦系數 • 良好的柔韌性 • 耐熱性，高
• 可加工性，良好 • 耐化學性良好 • 韌性良好
用途 • 電器導線絕緣材料 • 電線電纜應用
形式 • 顆粒料
加工方法 • 擠出
物理性能 額定值單位制 測試方法
比重 1.77g/cm³ ASTM D792
熔流率 (297°C/5.0 kg) 7.0g/10 min ASTM D1238
機械性能 額定值單位制 測試方法
抗張強度 ASTM D638
23°C 37.9MPa
140°C 11.4MPa
160°C 8.62MPa
180°C 6.21MPa
200°C 3.45MPa
伸長率 ASTM D638
斷裂, 23°C 300%
斷裂, 140°C 600%
斷裂, 160°C 650%
斷裂, 180°C 600%
斷裂, 200°C 600%
彎曲模量 645MPa ASTM D790
熱性能 額定值單位制
熔融溫度 219 到 254°C
可燃性 額定值單位制 測試方法
極限氧指數 34% ASTM D2863
補充信息
The values listed as Tensile Strength, ASTM D638, and Tensile Elongation @ Brk, ASTM D638, were tested in accordance with ASTM D1708. Specific Gravity, ASTM D792: 1.75 to 1.79 sp gr 23/23°C
MIT Flex Life: 120000
擠出 額定值單位制
第1氣缸區溫度 288°C
第2氣缸區溫度 316°C
第3氣缸區溫度 321°C
連接器溫度 321°C
熔體溫度 332 到 335°C
模具溫度 332°C
1 / 2
Tefzel 750 2012年9月30日
乙烯四氟乙烯共聚物
DuPont Fluoropolymers
備注
1 一般屬性：這些不能被視為規格。
|