NEOFLON™ AP-210
全氟烷氧基
DAIKIN AMERICA, INC.
產品說明
NEOFLON PFA is a copolymer of tetrafluoroethylene and perfluoroalkyl vinyl ether, NEOFLON PFA is a compound of carbon atoms and fluorine atoms in which a perfluoroalkoxy radical is bonded to the carbon chain in the following molecular structure.
NEOFLON PFA has better mechanical strength at high temperatures than NEOFLON FEP, and has excellent moldability for easy of processing by extrusion, compression, blow, transfer, and injection molding methods. Due to the high bonding strength of the carbon, fluorine and oxygen atoms, NEOFLON PFA demonstrates nearly the same outstanding capabilities as PTFE in temperatures ranging -200°C ~+260°C. NEOFLON PFA has excellent transparency for use in melt-flow processing.
總體
材料狀態 • 已商用：當前有效
供貨地區 • 北美洲
• Good Corrosion Resistance • 共聚物 • 耐氣候影響性能良好
性能特點 • 低摩擦系數 • 良好的成型性能 • 清晰度，高
• 高溫強度 • 良好的電氣性能 • 阻燃性能
用途 • 電線護套 • 涂敷應用
外觀 • 半透明 • 可用顏色
形式 • 顆粒料
加工方法 • 擠出 • 注射成型
物理性能 額定值單位制 測試方法
比重 2.14 到 2.16g/cm³ ASTM D792
表觀密度 1.00 到 1.40g/cm³ JIS K6891
熔流率 (372°C/5.0 kg) 10 到 17g/10 min ASTM D1238
吸水率 (飽和) < 0.010% ASTM D570
機械性能 額定值單位制 測試方法
抗張強度 (屈服) 25.4 到 30.4MPa JIS K6891
伸長率 (斷裂) 350 到 450% JIS K6891
彎曲模量 580 到 690MPa ASTM D790
壓縮模量 490 到 590MPa ASTM D695
壓縮強度 ASTM D695
1% 應變 4.90 到 5.90MPa
25% 應變 31.4 到 33.3MPa
摩擦系數 (與鋼 - 靜態) 0.040 到 0.050
負載變形 ASTM D621
25°C, 14 MPa 2 8.00 到 9.00%
25°C, 14 MPa 3 2.50 到 3.00%
100°C, 6.9 MPa 2 8.50 到 9.50%
100°C, 6.9 MPa 3 2.00 到 3.00%
Flexural Strength No break ASTM D790
沖擊性能 額定值單位制 測試方法
懸壁梁缺口沖擊強度 無斷裂 ASTM D256
硬度 額定值單位制 測試方法
硬度計硬度 (邵氏 D) 60 到 70 ASTM D2240
熱性能 額定值單位制 測試方法
熔融溫度 300 到 310°C ASTM D4591
線形膨脹系數 - 流動 (20 到 100°C) 0.00012cm/cm/°C ASTM D696
比熱 1050J/kg/°C
導熱系數 0.26W/m/K ASTM C177
可燃性 額定值單位制 測試方法
UL 阻燃等級 (1.57 mm) V-0 UL 94
極限氧指數 (1.57 mm) > 95% ASTM D2863
充模分析 額定值單位制
熔體粘度 (380°C) 2.00E+6 到 2.50E+7mPa•s
|