NEOFLON™ AP-211SH
全氟烷氧基
DAIKIN AMERICA, INC.
產(chǎn)品說(shuō)明
NEOFLON PFA is a copolymer of tetrafluoroethylene and perfluoroalkyl vinyl ether, NEOFLON PFA is a compound of carbon atoms and fluorine atoms in which a perfluoroalkoxy radical is bonded to the carbon chain in the following molecular structure.
NEOFLON PFA has better mechanical strength at high temperatures than NEOFLON FEP, and has excellent moldability for easy of processing by extrusion, compression, blow, transfer, and injection molding methods. Due to the high bonding strength of the carbon, fluorine and oxygen atoms, NEOFLON PFA demonstrates nearly the same outstanding capabilities as PTFE in temperatures ranging -200°C ~+260°C. NEOFLON PFA has excellent transparency for use in melt-flow processing.
總體
材料狀態(tài) • 已商用：當(dāng)前有效
供貨地區(qū) • 北美洲
• Good Corrosion Resistance • 高溫強(qiáng)度 • 耐氣候影響性能良好
• High Purity • 共聚物
性能特點(diǎn) • 清晰度，高
• 低摩擦系數(shù) • 良好的成型性能
• 阻燃性能
• 高 ESCR（抗應(yīng)力裂紋） • 良好的電氣性能
用途 • 半導(dǎo)體模制化合物
外觀 • 半透明 • 可用顏色
形式 • 顆粒料
加工方法 • 注射成型
物理性能 額定值單位制 測(cè)試方法
比重 2.14 到 2.16g/cm³ ASTM D792
表觀密度 1.00 到 1.40g/cm³ JIS K6891
熔流率 (372°C/5.0 kg) 10 到 18g/10 min ASTM D1238
吸水率 (飽和) < 0.010% ASTM D570
熱性能 額定值單位制 測(cè)試方法
熔融溫度 300 到 310°C ASTM D4591
線形膨脹系數(shù) - 流動(dòng) (20 到 100°C) 0.00012cm/cm/°C ASTM D696
比熱 1050J/kg/°C
導(dǎo)熱系數(shù) 0.26W/m/K ASTM C177
可燃性 額定值單位制 測(cè)試方法
UL 阻燃等級(jí) (1.57 mm) V-0 UL 94
極限氧指數(shù) (1.57 mm) > 95% ASTM D2863
充模分析 額定值單位制
熔體粘度 (380°C) 2.00E+6 到 2.50E+7mPa•s
|